Fluorocarbon fluoropolymer rubber for Bonding to Metal
Product Description |
Ingredients |
Copolymer of Vinylidene Fluoride and Hexafluoropropylene. Curing system, processing aids and filers contained. |
Features |
Proprietary curing agent compounding technology, excellent processing, mold release, mold flow and compression set properties. |
Processing |
Compression, transfer and injection molding. |
Application |
Suitable for make O-rings and oil seals. |
Curing system |
Bisphenol AF |
Lab Testing Curing condition |
Press cure 10 min @ 170ºC |
Post cure 20 hrs @ 230ºC |
Typical Rheological Properties |
Monsanto Moving Die Rheometer(MDR2000®)100cpm, 0.5°Arc,6 minutes@177ºC |
ML Minimum Torque, N·m |
0.23 |
|
|
MH Maximum Torque, N·m |
1.99 |
|
|
ts2 |
0'50'' |
|
|
T10 |
0'47'' |
|
|
t90 |
2'09'' |
|
|
|
|
|
|
Typical Original Properties |
Property |
Unit |
Test Method |
Typical Value |
Gravity |
g/cm3 |
ASTM D-297 |
1.9 |
Tensile Strength |
Mpa |
ASTM D-412 |
16.6 |
Elongation at break |
% |
ASTM D-412 |
211 |
Hardness |
Shore A |
ASTM D-2240 |
70+/-5 |
|
|
|
|
Hot Air Aging, 70 hrs @ 250ºC |
Hardness change |
Pt |
ASTM D-573 |
+2 |
Tensile strength change |
% |
ASTM D-573 |
-9 |
Elongation change |
% |
ASTM D-573 |
-5 |
|
|
|
|
Compression Set, 24 hrs @200ºC |
Compression Set |
% |
ASTM D-395B |
13.7 |